PEEK5600LF30 particles

PEEK5600LF30 (black) is a bearing grade plastic made by adding PTFE, graphite and carbon fiber. Its superior friction properties (low friction coefficient, wear resistance, and higher peak pressure limit) make it an ideal material for this level of friction applications. It is suitable for manufacturing wear-resistant strips, friction plates and other products.

Item	Test Standard or Instrument	Unit	PEEK5600LF30
			PEEK+30%(Carbon fiber+Graphite+PTFE)
Tensile strength(23℃)	ISO527-2/1B/50	MPa	145
Tensile modulus(23℃	ISO527-2/1B/51	GPa	14
Tensile elongation(23℃)	ISO527-2/1B/50	%	2.2
Bending strength(23℃)	ISO 178	MPa	220
Bending modulus(23℃)	ISO 178	GPa	12
Compressive strength(23℃)	ISO 604	MPa	170
Charpy tched impact strength( no gap)	ISO 179/U	KJ/m2	32
Lzod impact strength	ISO 180/A	KJ/m2	5

1、If you need other parameter, please contact us!

2、This performance index cannot be used as acceptance criteria.

 

Item	Test Standard or Instrument	Unit	PEEK5600LF30
			PEEK+30%(Carbon fiber+Graphite+PTFE)
Melting point	DSC	℃	343
Distortion temperature	ISO 75-1/-2	℃	315
Continuous using temperature	UL 74685	℃	260
Coefficient of thermal expansion	ASTM D696	ppm K-1	13
Flammable level	UL 94	/	V-0
Thermal conductivity	ISO 22007	W/（m·K）	0.86

 

Item	Test Standard or Instrument	Unit	PEEK5600LF30
			PEEK+30%(Carbon fiber+Graphite+PTFE)
Dielectric strength	IEC 60243-1	KV/mm	–
Dielectric constant	IEC 60250	–	–
Surface Resistance	IEC 61340	Oh	106
Lossy medium	IEC 60251	–	–

 

Item	Test Standard or Instrument	Unit	PEEK5600LF30
			PEEK+30%(Carbon fiber+Graphite+PTFE)
Color	–		black Black
Density	ISO 1183	g/cm3	1.44
Water Abs. (25℃.24Hrs)	ISO 62	%	0.05
Mould shrinking percentage	3mm,170℃, Flow direction	%	0.3
	Perpendicular to flow direction	%	0.9
Simeom Denis Poisson	ISO 527-2		0.35
Rockwell hardness	GB/T 3398.2	HRR	114
Friction coefficient	ASTM D3702	m	0.18
Melt flow index	ISO1133	g/10min	3

 

• FDA approved
• Low noise
• High strength
• Self-lubrication
• Impact resistance
• High purity
• Wear resistance
• High temperature resistance
• Lightweight
• Corrosion resistance
• Hydrolysis resistance
• Good biocompatibility