PEEK7600GF30 Particles

As an advanced engineering plastic, PEEK plays an important role in weight reduction, effective extension of component service life, and optimization of component utilization due to its good machinability, flame retardancy, non-toxicity, wear resistance, and corrosion resistance. With the acceleration of downstream application promotion, it is expected that China's PEEK demand will exceed 10,000 tons in 2022. 30% glass fiber + 70% PEEK, glass fiber plays a reinforcing role in the component, and its non-conductive characteristics are suitable for use in materials with high insulation requirements and strong rigidity. PEEK7600GF30 can be used for production and processing by injection molding and extrusion.

Item	Test Standard or Instrument	Unit	PEEK7600GF30
			Contains 30% glass fiber (PEEK+70%Glass fiber)
Tensile strength(23℃)	ISO527-2/1B/50	MPa	175
Tensile modulus(23℃	ISO527-2/1B/51	GPa	12.5
Tensile elongation(23℃)	ISO527-2/1B/50	%	2.8
Bending strength(23℃)	ISO 178	MPa	268
Bending modulus(23℃)	ISO 178	GPa	11.5
Compressive strength(23℃)	ISO 604	MPa	247
Charpy tched impact strength( no gap)	ISO 179/U	KJ/m2	58
Lzod impact strength	ISO 180/A	KJ/m2	10

1. Typical values ​​are injection molding indicators. If necessary, please call our technical department for more detailed technical indicators!

2. This performance index cannot be used as acceptance criteria.

Item	Test Standard or Instrument	(Unit	PEEK7600GF30
			PEEK+30%Glass fiber
Melting point	DSC	℃	343
Distortion temperature	ISO 75-1/-2	℃	330
Continuous using temperature	UL 74685	℃	260
Coefficient of thermal expansion	ASTM D696	ppm K -1	18
Flammable level	UL 94	/	V-0
Thermal conductivity	ISO 22007	W/（m·K）	0.30

 

Item	Test Standard or Instrument	Unit	PEEK7600GF30
			PEEK+30%Glass fiber
Dielectric strength	IEC 60243-1	KV/mm	17
Dielectric constant	IEC 60250	–	3.3
Surface resistance	IEC 61340	Oh	1013
Lossy medium	IEC 60251	–	0.005

 

Item	Test Standard or Instrument	Unit	PEEK7600GF30
			PEEK+30%Glass fiber
Color	–		Primary color, grayish yellow Natural
Density	ISO 1183	g/cm 3	1.5
Water Abs. (25℃.24Hrs)	ISO 62	%	0.05
Mould shrinking percentage	3mm thickness, flow direction at 170℃ 3mm,170℃, Flow direction	%	0.3
	Perpendicular to flow direction (Bigger after saturated crystallization) Perpendicular to flow direction	%	0.8
Simeom Denis Poisson	ISO 527-2		0.35
Rockwell hardness	GB/T 3398.2	HRR	120
Friction coefficient	ASTM D3702	m	0.35-0.4
Melt flow index	ISO1133	g/10min	2

 

• FDA approved
• Low noise
• High strength
• Self-lubrication
• Impact resistance
• High purity
• Wear resistance
• High temperature resistance
• Lightweight
• Corrosion resistance
• Hydrolysis resistance
• Good biocompatibility